한국표면공학회지 (21권4호 168-175)

Effect of Ultrasonic Wave on the Nickel-Zine Alloy Deposition whit the Variation of Ammonium Chloride Concertration

Ni-Zn 함금도금에서 염화암몬 농도에 따른 초음파의 영향

양학희;고광진;김재원;
;;;

인하전문대학;인하대학교 공과대학 금속공학과;
인하전문대학;인하대학교 공과대학 금속공학과;

Abstract

The nickel0zinc allot depositions have been studjen in ammonium chloridw added chloride baths to fine out the effects of ultrasonic irradiation for the electrodeposition processes. The compositions of deposited alloys, the current efficiencies, corrosion resistance and brightness in various conditions of electrodeposition were investigated, in the range of ultrasonic irradiation of 50,500 and 1,000kc/s respectively. The results obtained are as follows; 1. the ratio of nikel to zinc in the deposit increased according 시 the ammonium chloride concentration in irradiated baths. 2. The current efficiencies became also higer in the irradiated bath. 3. Ammonium ions in solution seem to retard formation of zinc hydroxide. 4. The corrsion resistance and brightness of the deposits are dependent upon nickel content of deposits which ranges 10-18%(wt)nickel in the irradiated baths and 11-15%(wt)in ninirradisted baths. 5. The corrosion resistance and brightnes of the deposited are appreciably better in the irradiated baths than in non-irradiated bath with the mole ratio of 3.4(NH+4/Ni+++Zn++).

Keywords